Pre Shaded 3D PRO Multilayer Dental Lab Zirconium Block Digital CAD Cam Zirconia Blank Disc

• Customization: Available
• Usage: Model Making, Veneers, Inlays, Onlays, Crowns, Bridges, Abutment
• Usage Times: Disposable
• Material: Zirconia
• Applicable Departments: Dental Laboratory
• Nature: Specialized Instrument Equipment
• Certification: CE
• Instrument Classification: Class II
• Model Number: 3D-PRO-Ml
• Power Source: Machinery
• Shelf Life: 3 Years
• Quality Certification: CE
• Size: 98mm 95mm 92mm
• Thickness: 10/12/14/16/18/20/22/25/30mm
• Color: Vita16
• Strength: 600MPa-1000MPa
• Translucency: 43%-49%
• Sku: W471-79
• Transport Package: Cardboard Box
• Trademark: Jinguang
• Origin: China
• Production Capacity: 50000 Pieces/Monthly

Product Description

Product Description

Pre Shaded 3D Pro Multilayer Dental Lab Zirconium Block Digital CAD CAM Zirconia Blank Disc
 

ST Zirconia Blocks

 

Dimensions: 98/95/92 x75mm

Translucency: 43%
Strength: ≥1200MPa
Thickness: 10/12/14/16/18/20/22/25mm

 

 

- High quality raw materials, excellent aging resistance.
- Combining aesthetic and strength performance indicators.
- The most commonly used white block material is preferred.

 

Physical Property		Chemical Composition
Density after sintering	≥6.09g/cm3	ZrO2 +HfO2 + Y2O3	≥99%
Fracture toughness	≥5.0MPa.m1/2	Y2O3	4.5%-6.0%
Hardness	(Hv10) 1250	AI2O3	<0.15%
Sintering temperature	1530ºC	Other oxides	<0.15%

 

ST-C Zirconia Blocks

 

Dimensions: 98/95/92 x75mm

Translucency: 43%
Strength: ≥1100MPa
Thickness: 10/12/14/16/18/20/22/25mm

 

 

- High quality raw materials, excellent anti-aging performance.
- Combining aesthetic and strength performance indicators.
- The most commonly used color block material for posterior teeth is preferred.

Physical Property		Chemical Composition
Density after sintering	≥6.09g/cm3	ZrO2 +HfO2 + Y2O3	≥99%
Fracture toughness	≥5.0MPa.m1/2	Y2O3	4.5%-6.0%
Hardness	(Hv10) 1250	AI2O3	<0.15%
Sintering temperature	1530ºC	Other oxides	<0.5%

 

3D-Pro-ML Zirconia Blocks

 

Dimensions: 98mm/95mm/92x75mm

Translucency: 43% -49%

Strength: 600MPa-1000MPa

Thickness: 10/12/14/16/18/20/22/25mm

 

 

- High quality raw materials, excellent chemical resistance.
- No hierarchical natural gradient, saving production time.
- Specially suitable for all zirconium aesthetic restoration of anterior teeth.

Physical Property		Chemical Composition
Density after sintering	≥6.05g/cm3	ZrO2 +HfO2 + Y2O3	≥99%
Fracture toughness	≥5.0MPa.m1/2	Y2O3	4.5%-8.0%
Hardness	(Hv10) 1250	AI2O3	<0.15%
Sintering temperature	1500ºC	Other oxides	<0.5%

Product Parameters

Product type	Translucency	Strength	Color	Sintering temperature
4D-Pro Multilayer	43%-49%	600-1050MPa	16 VITA+BL1-4	1500ºC
3D-Pro Multilayer	43%-49%	600-1000MPa	16 VITA+BL1-4	1500ºC
SHT	47%	≥900MPa	White	1530ºC
SHT-C	47%	≥800MPa	A1 A2 A3 B1 B2	1530ºC
SHT-ML	47%	≥800MPa	A1 A2 A3 B1 B2 BL1-4	1530ºC
ST	43%	≥1200MPa	White	1530ºC
ST-C	43%	≥1100MPa	16 VITA	1530ºC
ST-ML	43%	≥1100MPa	16 VITA	1530ºC
HT	39%	≥1350MPa	White	1530ºC
HT-C	39%	≥1350MPa	16 VITA	1530ºC

 