Dental Implant Titanium Blank 98mm Grade 5 for Dentist Open CAD Cam Milling System Titan Denture

• Customization: Available
• Usage: Dental Frameworks
• Usage Times: Disposable
• Material: Titanium
• Applicable Departments: Dental Laboratory
• Nature: Specialized Instrument Equipment
• Certification: CE
• Instrument Classification: Class I
• Model Number: A750
• Power Source: Machinery
• Shelf Life: 3 Years
• Quality Certification: CE
• Product Specification: 98mm
• Thickness: 10/12/14/16/18/20/22/25mm
• Applications: Dental CAD/Cam
• Sku: W432-09
• Transport Package: Cardboard Box
• Trademark: Jinguang
• Origin: China
• Production Capacity: 5000 Pieces/Monthly

Product Description

Product Description

S600 Grade 5 Titanium Alloy (Ti6Al4V ELI)

Use: for the production of dental frameworks

Size: 98x10/12/14/16/18/20/22/25mm

Features:

The composition is consistent with the main element, with a consistency of up to 99.5% across different batches; Impurity elements such as H and Si ensure double zero level; No cutting defects, dual ultrasonic and X-ray inspection; Microscopic structure with microcrystals exceeding grade A; High elasticity and strength comparable to cobalt chromium alloy; Excellent biocompatibility; Low thermal conductivity, high strength and low density, making it more comfortable to wear; Excellent microstructure and stability of major components, combined with cutting and processing Micro hardening during the process ensures a high surface finish.

Ingredient
Ti	88.5%
Al	5.5% - 6.5%
V	3.5% - 4.5%
Beneficial interstitial element	≤ 0.5%
Impurity	≤ 0.05%
Performance
Tensile strength	≥1100Mpa
Vickers hardness (Hv10)	≥ 310
Coefficient of thermal expansion	9.9 X 10-6.k-1
Density	4.43g/cm3

 

A750 Grade 5 Titanium Alloy (Ti6Al4V ELI)

Use: for the production of dental frameworks and implant abutments super structions

Size: 98x10/12/14/16/18/20/22/25mm

Features:

Medium strength and hardness, reducing polishing workload and improving processing efficiency; Better biocompatibility and excellent; The composition is uniform, and the consistency of the main elements in different batches is as high as 99.7%; Impurity elements such as H and Si ensure double zero level; No cutting defects, dual ultrasonic and X-ray inspection; Microscopic structure with microcrystals exceeding grade A; Low thermal conductivity, high strength and low density, making it more comfortable to wear; Damage tolerance design, more reliable foundation and support, and higher fatigue life; The crown bridge has no residual stress, higher machining accuracy, and is more comfortable to wear.

Ingredient
Ti	88.5%
Al	5.5% - 6.5%
V	3.5% - 4.5%
Beneficial interstitial element	≤ 0.5%
Impurity	≤ 0.04%
Performance
Tensile strength	≥1100Mpa
Vickers hardness (Hv10)	≥ 310
Coefficient of thermal expansion	9.9 X 10-6.k-1
Density	4.43g/cm3

Company Profile